Tabular alumina is a high-level synthetic refractory raw material, characterized by its superior performance advantages, including high refractoriness, low alkali content, high strength, high thermal shock resistance, excellent slag attack resistance and high-temperature volumetric stability. These advantages are attributed to its engineered microstructure, featured in well-developed crystal grains and uniformly distributed intracrystalline micropores.
Tabular alumina is a high-level synthetic refractory raw material, characterized by its superior performance advantages, including high refractoriness, low alkali content, high strength, high thermal shock resistance, excellent slag attack resistance and high-temperature volumetric stability. These advantages are attributed to its engineered microstructure, featured in well-developed crystal grains and uniformly distributed intracrystalline micropores.
The automation level, technique level and product quality of Jingxin's tabular alumina production are all at advanced levels both domestically and internationally, and this product has been well sold to over 400 customers worldwide.
It is widely used in refractories for high-temperature industries, including steelmaking, nonferrous metallurgy, petrochemical, foundry, glass, cement, garbage incineration sectors and other high-temperature industrial fields.
|
Chemical composition |
Unit |
Grain |
-0.1mm |
-20μm |
|
Al2O3 |
% |
99.5 |
99.4 |
99.3 |
|
Na2O |
% |
≤ 0.40 |
≤ 0.40 |
≤ 0.40 |
|
SiO2 |
% |
≤ 0.08 |
≤ 0.10 |
≤ 0.10 |
|
Fe2O3 |
% |
≤ 0.06 |
≤ 0.08 |
≤ 0.08 |
|
Magnetic Fe |
% |
≤ 0.02 |
≤ 0.02 |
≤ 0.02 |
|
Physical properties |
||||
|
Bulk density |
g/cm3 |
≥ 3.50 |
|
|
|
Apparent porosity |
% |
≤ 5.00 |
|
|
|
Water absorption |
% |
≤ 1.50 |
|
|
Fines: -200mesh，-325mesh
Packing: 25kg bag/1000kg big bag/ as per customer’s request